Image icon  Al-90 wt% Cu (bronze)

 
Use this resource: Use this resource icon
Link to this page: http://core.materials.ac.uk/search/detail.php?id=1697
View at:            
Resource type: Image
Description: This is a copper-aluminium bronze containing 10 wt% aluminium. A small amount of iron is often added to act as a grain refiner to improve the mechanical properties. Alloys with more than 8 wt% aluminium solidify as the β phase. Below about 930°C, Widmanstätten α phase precipitates. At the eutectoid temperature (565°C) the remaining β decomposes to a lamellar eutectoid of α and β. Rapid cooling from the high temperature β phase can form martensite instead of Widmanstätten α. Aluminium bronzes have high strength, corrosion resistance and good high temperature properties (up to 300-400°C). Typical applications include bearings, gears and corrosion resistant vessels.
Keywords: alloy • aluminium • bronze • copper • corrosion resistance • lamella • martensite • metal • Widmanstä • tten
Categories: Science approaches > Microstructure
Materials > Metals & alloys > Copper & alloys
Testing, analysis & experimentation > Metallography
Scale > Micro
Created by: DoITPoMS, University of Cambridge
Dr J Marrow, Department of Materials Science, University of Manchester and UMIST
Published by: DoITPoMS, University of Cambridge
License: This resource is released under the Creative Commons Attribution Non-Commercial Share Alike license (2.0 UK: England & Wales).
Creative Commons Attribution Non-Commercial Share Alike logo
You are free:
  • to share – to copy, distribute and transmit the work
  • to remix – to adapt the work
Under the following conditions:
  • attribution – You must attribute the work in the manner specified by the author or licensor (but not in any way that suggests that they endorse you or your use of the work).
  • noncommercial – You may not use this work for commercial purposes.
  • share alike – If you alter, transform, or build upon this work, you may distribute the resulting work only under the same or similar license to this one.
View the full legal code here.
Date created: 07 November 2002
Date added: 21 August 2009
Package:
Resource ID: 1697