Image icon  Cu-4.5 wt% P

 
Use this resource: Use this resource icon
Link to this page: http://core.materials.ac.uk/search/detail.php?id=1726
View at:            
Resource type: Image
Description: This is an example of a hypoeutectic alloy. On slow cooling the liquid first solidified at approximately 940°C as copper rich dendrites. The composition of the remaining liquid became increasingly rich in phosphorus until it solidified as a eutectic (8.38 wt% P) at the eutectic temperature of 714°C. Note that the dendrites are cored - the different contrast after etching indicated that the composition varies with position in the dendrites. This is caused by non-equilibrium solidification. The cooling rate was too rapid for equilibrium to be maintained between the solid and the liquid phases.

This alloy has no practical applications. Phosphor bronzes usually contain 5 wt% Sn for solid solution strengthening with 0.2 wt% P for interstitial solution strengthening. They have high strength and corrosion resistance and are usually used for springs.
Keywords: alloy • bronze • copper • coring • dendrite • hypoeutectic • metal • phosphorus
Categories: Science approaches > Microstructure
Materials > Metals & alloys > Copper & alloys
Testing, analysis & experimentation > Metallography
Scale > Micro
Created by: Dr J Marrow, Department of Materials Science, University of Manchester and UMIST
DoITPoMS, University of Cambridge
Published by: DoITPoMS, University of Cambridge
License: This resource is released under the Creative Commons Attribution Non-Commercial Share Alike license (2.0 UK: England & Wales).
Creative Commons Attribution Non-Commercial Share Alike logo
You are free:
  • to share – to copy, distribute and transmit the work
  • to remix – to adapt the work
Under the following conditions:
  • attribution – You must attribute the work in the manner specified by the author or licensor (but not in any way that suggests that they endorse you or your use of the work).
  • noncommercial – You may not use this work for commercial purposes.
  • share alike – If you alter, transform, or build upon this work, you may distribute the resulting work only under the same or similar license to this one.
View the full legal code here.
Date created: 07 November 2002
Date added: 21 August 2009
Package:
Resource ID: 1726