Image icon  IN718 nickel-based superalloy held for 20 minutes at 850°C

 
Use this resource: Use this resource icon
Link to this page: http://core.materials.ac.uk/search/detail.php?id=1743
View at:            
Resource type: Image
Description: IN718 is a nickel-based superalloy composed of approximately 53 wt% Ni, 19 wt% Fe, 18 wt% Cr, 5 wt% Nb, and small amounts of Ti, Mo, Co, and Al. The alloy has a number of distinct phases present in its microstructure. These are namely the matrix, γ, and the precipitates, γ', γ'', and δ.

The primary strengthening phase is γ'' [1], the composition of which is Ni3Nb. It has a body-centred tetragonal structure, and forms semi-coherently as disc-shaped platelets within the γ matrix, having three variants lying on the {100} planes. It is stable for over 10,000 hours at 600°C; however, above this temperature it decomposes to form γ', Ni3Al (between 650°C and 850°C), and δ, the same composition as γ'' (between 750°C and 1000°C). It has been commented that, at large volume fractions and when it forms continuously along grain boundaries, δ is detrimental to both strength and toughness [2].

The δ phase that forms is more stable than the γ'' phase, and has an orthorhombic structure. During cooling, δ phase precipitates begin to form along the {111} planes in the matrix, nucleating at grain boundaries at approximately 1010°C.

The γ' precipitates, of L12 structure, are seen within the γ matrix when it has been depleted of niobium due to the formation of γ'' and δ.

The Time-Temperature-Transformation (TTT) diagram for IN718 shows that δ precipitates at higher temperatures than the γ'', and that over long periods of time both δ and γ' are more stable than γ''.

The micrograph shows the microstructure after being held for 20 minutes at 850°C, and it can be seen that small γ'' precipitates have precipitated out within the matrix.

References:

[1] J. W. Brooks and P. J. Bridges. Metallurgical Stability of Inconel Alloy 718. Superalloys '88, pages 33-42, 1988.
[2] B. Gleeson. High-Temperature Corrosion of Metallic Alloys and Coatings: Volume II. In M. Schütze, editor, Corrosion and Environmental Degradation, volume 19 of Materials Science and Technology, chapter 5, pages 173 - 228. Wiley, 2000.

Keywords: alloy • metal • nickel • nickel-based superalloy • niobium • precipitation
Categories: Science approaches > Microstructure
Materials > Metals & alloys > Nickel & alloys
Testing, analysis & experimentation > Metallography
Scale > Micro
Created by: DoITPoMS, University of Cambridge
R Guest, Rolls-Royce University Technology Centre, Department of Materials Science and Metallurgy, University of Cambridge
Published by: DoITPoMS, University of Cambridge
License: This resource is released under the Creative Commons Attribution Non-Commercial Share Alike license (2.0 UK: England & Wales).
Creative Commons Attribution Non-Commercial Share Alike logo
You are free:
  • to share – to copy, distribute and transmit the work
  • to remix – to adapt the work
Under the following conditions:
  • attribution – You must attribute the work in the manner specified by the author or licensor (but not in any way that suggests that they endorse you or your use of the work).
  • noncommercial – You may not use this work for commercial purposes.
  • share alike – If you alter, transform, or build upon this work, you may distribute the resulting work only under the same or similar license to this one.
View the full legal code here.
Date created: 28 January 2003
Date added: 21 August 2009
Package:
Resource ID: 1743